SKF bearing grease LGHB 2 in 18 kg pail |
| Subtitle |
SKF High Load, High Temperature, High Viscosity Bearing Grease NLGI 2 |
| Description |
SKF LGHB 2 is a high viscosity, mineral oil based grease, using the latest complex calcium-sulphonate soap technology. Formulated to withstand high temperatures and extreme loads, it is suitable for a wide range of applications, especially in cement, mining and metal segments. This grease contains no additives and the extreme pressure properties arise from the soap structure.<br/><strong>Typical applications:</strong><br/>• Steel on steel plain bearings<br/>• Pulp and paper making machines<br/>• Asphalt vibrating screens<br/>• Continuous casting machines<br/>• Sealed spherical roller bearings operating up to 150 °C (300 °F)<br/>• Work roll beaings in steel industry<br/>• Mast rollersnof fork lift trucks |
| Features |
• Excellent load capacity, anti-oxidation and corrosion protection even with large water ingress<br/>• Withstands peak temperatures of 200 °C (390 °F) |
| Product Page Url |
http://www.skf.com/group/products/lubrication-solutions/lubricants/high-load-high-temperature-high-viscosity-grease/index.html |
| Grease Name |
LGHB 2 |
| Nlgi Consistency Class |
2 |
| Thickener |
Complex calcium sulphonate |
| Base Oil Type |
Mineral |
| Colour |
Brown |
| Operating Temperature Range |
-20 to +150 °C |
| Base Oil Viscosity |
400-450 cSt at 40 °C; 26,5 cSt at 100 °C |
| Dropping Point Din Iso 2176 |
> 220 °C |
| Din 51825 Code |
KP2N-20 |
| Penetration Din Iso 2137 |
60 strokes, 10<sup>-1</sup> mm: 265-295: 100000 strokes, 10<sup>-1</sup> mm: - 20 to + 50 (325 max.) |
| Roll Stability Astm D1831 |
72 hours at 100 °C, 10<sup>-1</sup> mm: - 20 to + 50 change |
| Skf V2F Test |
'M' |
| Corrosion Protection Iso 11007 |
Standard (distilled water): 0-0; Water wash out: 0-0; Salt water test (100% salt water): 0-0 |
| Water Resistance Din 51 8071 |
3 hours at 90 °C: 1 max. |
| Oil Separation Din 51 817 |
7 days at 60 °C: 1-3 % |
| Skf R2F Test |
Running test B at 140 °C: Pass |
| Copper Corrosion Din 51811 |
2 max. at 150 °C |
| Ep Performances Din 51350 |
Wear scar DIN 51350/5,1400N: 0.86 mm; 4-ball test, welding load DIN 51350/4: > 4000 N |
| Rolling Bearing Grease Life |
ROF test, L<sub>50</sub> life at 10000 r/min: > 1000 hrs at 130 °C |
| Fretting Corrosion Astm D4170 Fafnir Test |
0 mg |
| Packsize |
18 kg pail |
| Available Packsizes |
420 ml cartridge (LGHB 2/0.4); 5 kg can (LGHB 2/5); 18 kg pail (LGHB 2/18); 50 kg drum (LGHB 2/50); 180 kg drum (LGHB 2/180) |
| Available For Single Point Lubrication |
SYSTEM 24 - LAGD: 60 ml (LAGD 60/HB2); SYSTEM 24 - LAGD: 125 ml (LAGD 125/HB2); SYSTEM 24 - TLSD: lubricator with 125 ml (TLSD 125/HB2); SYSTEM 24 - TLSD: lubricator with 250 ml (TLSD 250/HB2); SYSTEM 24 - TLSD: refill set 125 ml (LGHB 2/SD125); SYSTEM 24 - TLSD: refill set 250 ml (LGHB 2/SD250); TLMR: 380 ml cartridge (LGHB 2/MR380); TLMR: 380 ml cartridge with batteries (LGHB 2/MR380B) |
| Shelf Life |
5 years |